Effect of bisphenol-A on the structures and properties of phthalonitrile-based resin containing benzoxazine
Phthalonitrile and benzoxazine have been considered as high-performance materials in the field of heterocyclic chemistry. The polymerization of phthalonitrile and benzoxazine accelerated by active phenolic hydroxyl has attracted wide interests. In this work, self-promoted polymerization behavior and...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Budapest University of Technology and Economics
2015-06-01
|
| Series: | eXPRESS Polymer Letters |
| Subjects: | |
| Online Access: | http://www.expresspolymlett.com/letolt.php?file=EPL-0005900&mi=cd |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Phthalonitrile and benzoxazine have been considered as high-performance materials in the field of heterocyclic chemistry. The polymerization of phthalonitrile and benzoxazine accelerated by active phenolic hydroxyl has attracted wide interests. In this work, self-promoted polymerization behavior and processability of phthalonitrile containing benzoxazine (BA-ph) with bisphenol-A (BPA) were investigated. Results revealed that BA-ph/BPA exhibited representative doublestage curing behaviors corresponding to the ring-opening polymerization of benzoxazine rings and ring-formation polymerization of nitrile groups. Compared with that of BA-ph, processability of BA-ph/BPA was improved and could be tuned by varying BPA contents, processing temperature and time. Then BA-ph/BPA/glass fiber (GF) composite laminates were prepared. In comparison with that of BA-ph/GF laminates (542 MPa and 25.8 GPa), the flexural strength and modulus were up to 789 MPa and 23.6 GPa, respectively. Moreover, double Tgs were observed at temperature around 200~300°C and 300~380°C, indicating microphase separation during the polymerization of oxazine rings and nitrile groups, confirmed by the scanning electron microscopic (SEM) images. Thermal stabilities demonstrated that all BA-ph/BPA/GF composites exhibited high T10% up to 510°C. The systematic study of BA-ph/BPA system could enrich our knowledge on phthalonitrile-based resins in industrial applications, especially in the areas which require excellent mechanical properties and high temperature resistance. |
|---|---|
| ISSN: | 1788-618X |