Achieving 0.05 Ω-mm contact resistance in non-alloyed Ti/Au ohmics to β-Ga2O3 by removing surface carbon

Achieving 0.05 Ω-mm contact resistance in non-alloyed Ti/Au ohmics to β-Ga2O3 by removing surface carbon

Preserving a contamination-free metal–semiconductor interface in β-Ga2O3 is critical to achieve consistently low resistance (< 1 Ω-mm) ohmic contacts. Here, we report a scanning transmission electron microscopy study on the variation in Ti/Au ohmic contact quality to (010) β-Ga2O3 in a convention...

Full description

Saved in:
Bibliographic Details
Main Authors: Naomi Pieczulewski, Kathleen T. Smith, Corey M. Efaw, Arjan Singh, Cameron A. Gorsak, Joshua T. Buontempo, Jesse Wensel, Kathy Azizie, Katie Gann, Michael O. Thompson, Darrell G. Schlom, Farhan Rana, Hari P. Nair, Steven M. Hues, Elton Graugnard, Paul H. Davis, Debdeep Jena, Huili Grace Xing, David A. Muller
Format: Article
Language:English
Published: AIP Publishing LLC 2025-06-01
Series:APL Materials
Online Access:http://dx.doi.org/10.1063/5.0276786
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Preserving a contamination-free metal–semiconductor interface in β-Ga2O3 is critical to achieve consistently low resistance (< 1 Ω-mm) ohmic contacts. Here, we report a scanning transmission electron microscopy study on the variation in Ti/Au ohmic contact quality to (010) β-Ga2O3 in a conventional lift-off vs a metal-first process. We observe a thin ∼1 nm carbon barrier between the Ti and Ga2O3 in a non-conductive contact fabricated by a conventional lift-off process, which we attribute to photoresist residue, not previously detected by x-ray photoelectron spectroscopy due to the thinness and patchy coverage of the carbon layer, as well as roughness of the Ga2O3 surface. This thin carbon barrier is confirmed by electron energy loss spectroscopy and atomic force microscopy-infrared spectroscopy. We believe that the presence of the thin and patchy carbon layer leads to the highly inconsistent contact behavior in previous reports on non-alloyed contacts. Adventitious carbon is also observed in a conductive ohmic contact metal-first processing on an as-grown sample. We find that a five minute active oxygen descum is sufficient to remove this carbon on as-grown samples, further improving the ohmic behavior and reducing the contact resistance Rc to 0.06 Ω-mm. We also show that an hour long UV-ozone treatment of the Ga2O3 surface can eliminate carbon residue from the lift-off processing, resulting in a low Rc of 0.05 Ω-mm.