Reduced graphene oxide-ZnO hollow microsphere composite for supercapacitor applications
Through a facile solvothermal synthesis process, a reduced graphene oxide-ZnO microsphere composite was produced at 180 °C for 24 hours. Raman spectroscopy, X-ray diffraction, field emission scanning electron microscopy, and transmission electron microscopy were used to analyze the morphological str...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Universitas Mercu Buana
2025-05-01
|
| Series: | Jurnal Ilmiah SINERGI |
| Subjects: | |
| Online Access: | https://publikasi.mercubuana.ac.id/index.php/sinergi/article/view/31776 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Through a facile solvothermal synthesis process, a reduced graphene oxide-ZnO microsphere composite was produced at 180 °C for 24 hours. Raman spectroscopy, X-ray diffraction, field emission scanning electron microscopy, and transmission electron microscopy were used to analyze the morphological structures of the material. The analysis revealed that hexagonal phase wurtzite ZnO nanoparticles assembled homogeneous microspheres, decorated on the graphene sheets by graphene oxide functional groups. The ZnO nanoparticles are about 30 nm in size and the microspheres are hollow. A possible growth mechanism for the formation of ZnO hollow microspheres anchored on graphene sheets has been proposed. Cyclic voltammetry, galvanostatic charge-discharge and electrochemical impedance were used to evaluate the electrochemical performance of the composite. At a scan rate of 1 mV/s, the reduced graphene oxide-ZnO hollow microsphere composite electrode demonstrated an enhanced specific capacitance of 40.70 F/g with energy and power densities of 5.75 Wh/kg and 1.97 kW/kg, respectively. |
|---|---|
| ISSN: | 1410-2331 2460-1217 |